Nickel

K500

Available in bar dimensions of 63.5 mm (2.5") to 355.6 mm (14")

Length range up to 9.14 m (30')

Chemical Composition

C Mn Mo Cr Ni Cu Ti P S Si V Al
Min - - - - - - - - - - - -
Max 0.180 1.500 - - 63.000 33.000 0.850 - 0.010 0.500 - 3.150

Mechanical Properties

Tensile Strength 931 MPa min 135,000 psi min
Yield Strength 655 MPa min -
  95,000 psi min -
Total Elongation Under Load 20.000 % -
Hardness 35 Max HRC -

925

Available in bar dimensions of 63.5 mm (2.5") to 355.6 mm (14")

Length range up to 9.14 m (30')

Chemical Composition

C Mn Mo Cr Ni Cu Ti P S Si V Al
Min - - 2.500 19.500 - - - - - - - -
Max 0.030 1.000 3.500 22.500 46.000 3.000 2.400 0.030 0.030 0.500 - 0.500

Mechanical Properties

Tensile Strength 965 MPa min 140,000 psi min
Yield Strength 758 MPa min -
  110,000 psi min -
Total Elongation Under Load 20.000 % -
Hardness 38 Max HRC -

825

Available in bar dimensions of 63.5 mm (2.5") to 355.6 mm (14")

Length range up to 9.14 m (30')

Chemical Composition

C Mn Mo Cr Ni Cu Ti P S Si V Al
Min - - 2.500 19.500 - - - - - - - -
Max 0.050 1.000 3.500 23.500 46.000 3.000 1.200 - 0.030 0.500 - 0.200

Mechanical Properties

Tensile Strength 586 MPa min 85,000 psi min
Yield Strength 241 MPa min -
  35,000 psi min -
Total Elongation Under Load 30.000 % -
Hardness 35 Max HRC -

625

Available in bar dimensions of 63.5 mm (2.5") to 355.6 mm (14")

Length range up to 9.14 m (30')

Chemical Composition

C Mn Mo Cr Ni Cu Ti P S Si V Al
Min - - 8.000 20.000 - - - - - - - -
Max 0.100 0.500 10.000 23.000 58.000 - 0.400 0.015 0.015 - - 0.400

Mechanical Properties

Tensile Strength 827 MPa min 120,000 psi min
Yield Strength 414 MPa min -
  60,000 psi min -
Total Elongation Under Load 20.000 % -
Hardness 35 Max HRC -

718

Available in bar dimensions of 63.5 mm (2.5") to 355.6 mm (14")

Length range up to 9.14 m (30')

Chemical Composition

C Mn Mo Cr Ni Cu Ti P S Si V Al
Min - - 2.800 17.000 - - - - - - - -
Max 0.045 0.350 3.300 21.000 55.000 0.230 1.150 0.010 0.010 0.350 - 0.600

Mechanical Properties

Tensile Strength 1034 MPa min 150,000 psi min
Yield Strength 862 MPa min 1,000 MPa max
  125,000 psi min 145,000 psi max
Total Elongation Under Load 20.000 % -
Hardness 40 Max HRC -